cw 711 r, cz 112, naval brass, naval brass manufacturers, naval brass exporters, forging brass rods, brass forging rods, modified forging bras, bs 218, en 12164 1998, is 6912 2005 flb, brass extrusion rods, Brass hollow rods, brass hollow sections, brass extruded rods, brass extrusion sections, brass extrusion profiles, brass knurling rods, brass ingots, brass billets, Brass Extrusion Coil Wires, brass extrusions, brass profiles, brass sections, brass flats

CW711R is a type of Naval Brass with a copper and tin content lesser than that of CW712R. However, it does contain a certain amount of Lead percentage higher than CW712R. Apart from this difference in the chemical composition, it has almost the same properties as CW712R to withstand against corrosion resistance and excellent for hot forming applications.

Equivalent Specifications:

CW711R

UNS C 48500

Chemical Composition

Copper	59 to 62%
Tin	0.5 to 1.00%
Lead	0.50 to 1.00%
Iron	0.10% Max
Other Impurities	0.20% Max
Zinc	Remainder

Key Features:

» Excellent Hot Forming Capacity.

» High Strength Properties.

» Good Corrosion Resistance To Withstand in Sea Water.

» Excellent for Silvery Alloy Brazing and Soldering.

Physical Properties:

Tensile Strength	390 Mpa Min.
Elongation	20 Min.

Typical Applications:

Naval Brass generally finds its applications in the areas related to its name mainly Marine. It is used for Heat exchanger tubes, propeller shafts, condenser plates, marine hardware, bearings, pressure vessels and plumbing fittings.